ZGM95G 立磨 - 陶瓷复合辊套 / 碾底衬板使用实例
the use of examples-MMC Mill Roller / liner (ceramic insert roller / liner)
•
物料
=4500
大卡煤(
HGI=60
)
Material =4500 calories (hgi=60)
•
进料粒度
= 30-50mm Feed size =30-50 mm
•
磨损形式
=
高应力碾碎式磨粒磨损
Wear form = high stress crushed abrasive wear (grinding abrasion)
•
使用者及设备
=
燃煤热电厂
ZGM95G
立磨辊套
/
碾底衬板
equipment = ZGM95 vertical mill for coal-fired thermal power plants
•
高铬铸铁辊套使用寿命
= 6000-8000
小时
每千小时磨耗
=10-15mm
•
The service life of high chromium cast iron roller sleeve =6000-8000 hours =10-15 mm per 1000 hours
•
DJM
高铬陶瓷复合辊套使用寿命
=15000-30000
小时
每千小时磨耗
=2-3mm
•
DJM high chromium ceramic composite roller sleeve service life =15000-30000 hours per 1000 hours wear =2-3 mm
•
•
物料
=
水泥生料
Materials = Cement Raw Materials
•
莫氏硬度
=6-7 Moh hardness =6-7
•
进料粒度
= 30-50mm Feed size =30-50 mm
•
磨损形式
=
高应力碾碎式磨粒磨损
Wear form = high stress crushed abrasive wear (grinding abrasion)
•
使用者及设备
=
水泥厂
ZGM95G
立磨辊套
/
碾底衬板
equipment = ZGM95 vertical mill for coal-fired thermal power plants
•
高铬铸铁辊套使用寿命
= 4500-5000
小时
每千小时磨耗
=15-18mm
•
DJM
高铬陶瓷复合辊套使用寿命
=8000-12000
小时
每千小时磨耗
=4-6mm